EA 400 / 800
New conductive film.
Succussed in 105 ~ 106 conductivity with maintaining the transparency.
Mantain conductivity after forming.
The best for reuse, Excellent in washability and IPA-Proof.
| ITEM | Method / Unit / Content / Element | EA 400 | EA 800 |
| Width | mm | 510 ~ 700 | 510 ~ 700 |
| Thickness | mm | 0.5 ~ 1.0 | 0.5 ~ 1.0 |
| Specific Gravity | - | 1.34 | 1.34 |
| Surface Resistance | Ω / □ | 1 x 103 ~ 106 | 1 x 106 ~ 108 |
| Water Resistance | For 5 hrs afterdropping water | ○ | ○ |
| I P A Dropping | Wipe out after dried at room temperature | ○ | ○ |
| I P A Wiping Off | Wipe out with the cloth containing IPA | ○ | ○ |
| I P A Soaking | 5hrs | ○ | ○ |
| Methanol Soaking | 24hrs | ○ | ○ |
| Repetitive Washability | Ultrasonic Cleansing 1min x 10times | ○ | ○ |
| Decrement Time 5000V → 50V 27℃ 50% |
sec | 0.01 0.01 |
0.01 0.01 |
| Decrement Time 1000V → 10V 27℃ 50% |
sec | ○ | ○ |
| ITEM | Content / Element / Unit | Result | Analysis / Test Method |
|
Solvent Extraction Test FT-IR Analysis (Methanol 24 hrs at room temperature) |
Organic Compound | N / D | Solvent Extract Test (Methanol Room Temperature 24hrs) |
| Silicone Compound | N / D | FT-IR Analysis | |
| Aulfuric acid Ion | N / D |
Pure Water Extraction (80℃ x 1hr) Ion Chromalography DICNEXDX-120 |
|
| Bromide Ion | N / D | ||
| Fluorime Ion | N / D | ||
| Chioride Ion | N / D | ||
| Nitrate Ion | N / D | ||
| Cyanide Ion | N / D | ||
| Ammonium Ion | N / D | ||
| Resistance To IPA | IPA | No Change | 24hrs Srosion |
| Washability | Surface resistance has no change after 7 times washing | 5mins Ultrasonic Cleansing at room temperature After wiping out, Dry 100℃ x 1min |